Cracked in sharp cornes - Tool steels - Fractography - Heat treatment defects
Figure 1: This die, made of manganese oil-hardening stccl, cracked in sharp cornes because it was not tempered
immediately after the quench.
Defect name: Crack
Record No.: 2875
Type of defect (Internal/Surface): Surface
Defect classification: Fractography, heat treatment defects
Steel name: Tool steel
Steel composition in weight %: No data.
Note: No data.
Reference: Not shown in this demonstration version.