Drawing Defects

Breaks at the bending - 1.7102 steel - Cold drawing defects
Broken helical spring - 1.7176 steel - Cold drawing defects
Broken nitrided case - 1.7131 steel - Cold drawing defects
Burst at the bulging - 1.7709 steel - Cold drawing defects
Burst of screw head at the compression - 1.7034 steel - Cold drawing defects
Burst of screw head at the compression - 1.7076 steel - Cold drawing defects
Burst of screw head at the compression - 1.7034 steel - Cold drawing defects
Burst open upsetting sample - 1.4301 steel - Cold drawing defects
Burst open upsetting sample - 1.4303 steel - Cold drawing defects
Burst open upsetting sample - 1.4303 steel - Cold drawing defects
Central bursting in 4615 modified ball studs due to segregation - Drawing defects
Chromium oxide on the surface - 1.4016 steel - Cold drawing defects
Coarse grain - Wire rod defects - Drawing defects
Common defects - Drawing defects
Core segregation - Wire rod defects - Drawing defects
Core segregation with sulfide accumulation - 1.4105 steel - Cold drawing defects
Corner cracks at the drawing - 1.4122 steel - Cold drawing defects
Corroded plate surface - 1.4301 steel - Cold drawing defects
Cracks - Wire rod defects - Drawing defects
Cracks by internal defect - 1.4122 steel - Cold drawing defects
Cracks, longitudinal and transverse I - Drawing defects
Cracks, longitudinal and transverse II - Drawing defects
Displaced segregation - Wire rod defects - Drawing defects
Drawn-in drawing agent - 1.4301 steel - Cold drawing defects
Drawn-in scale - 1.2826 steel - Cold drawing defects
End cracking - Drawing defects
Fatigue fracture at a screw - 1.5511 steel - Cold drawing defects
Fins - Drawing defects
Fins - Wire rod defects - Drawing defects
Fire crack transfer marks - Wire rod defects - Drawing defects
Flat roll scratch - 1.4401 steel - Cold drawing defects
Flat roll scratch - 1.7034 steel - Cold drawing defects
Foreign material in the surface - 1.7225 steel - Cold drawing defects
Formation of friction martensite at the drawing - 1.6582 steel - Cold drawing defects
Fused-in extraneous matter - Wire rod defects - Drawing defects
Grain boundary attack - 1.4301 steel - Cold drawing defects
Grain boundary attack - 1.4303 steel - Cold drawing defects
Grain boundary damage - Wire rod defects - Drawing defects
Groove defect by shelling at the roll - 1.7139 steel - Cold drawing defects
Hard spots - Wire rod defects - Drawing defects
Hardening stress crack - 1.7035 steel - Cold drawing defects
Hot shortness and burnt - Wire rod defects - Drawing defects
Intercrystalline corrosion - 1.4105 steel - Cold drawing defects
Laps - Drawing defects
Laps - Wire rod defects - Drawing defects
Large slag line - 1.5919 steel - Cold drawing defects
Lines with strong pickling attack - 1.4401 steel - Cold drawing defects
Material breaks at the drawing - 1.2249 steel - Cold drawing defects
Mechanical damage - 1.7225 steel - Cold drawing defects
Mechanical damage - Wire rod defects - Drawing defects
Mechanical damage of the surface - 1.7076 steel - Cold drawing defects
Non-metallic inclusions - Wire rod defects - Drawing defects
Overlap by an surface near slag - 1.4105 steel - Cold drawing defects
Overpickled surface - 1.4305 steel - Cold drawing defects
Pincher - 1.2381 steel - Cold drawing defects
Pincher - 1.2842 steel - Cold drawing defects
Pincher - 1.4016 steel - Cold drawing defects
Pincher - 1.4104 steel - Cold drawing defects
Pincher - 1.4113 steel - Cold drawing defects
Pincher - 1.7034 steel - Cold drawing defects
Pincher - 1.7076 steel - Cold drawing defects
Pipe - Wire rod defects - Drawing defects
Pointed roll scratch - 1.8519 steel - Cold drawing defects
Pores in the core - 1.2379 steel - Cold drawing defects
Pre-material defect , cracks at the billet - 1.6582 steel - Cold drawing defects
Pre-material defect on the billet - 1.7034 steel - Cold drawing defects
Pre-material defect, scabs - 1.4305 steel - Cold drawing defects
Pressed in rolling fin - 1.7709 steel - Cold drawing defects
Rest of scale after the grinding - 1.4305 steel - Cold drawing defects
Rest of scale after the pickling - 1.4301 steel - Cold drawing defects
Rest of scale on the wire surface - 1.8523 steel - Cold drawing defects
Roll marks - Wire rod defects - Drawing defects
Roll scratch - 1.7139 steel - Cold drawing defects
Rolled in foreign material - 1.7076 steel - Cold drawing defects
Rolled in foreign material - 1.7709 steel - Cold drawing defects
Rolled-in extraneous matter - Wire rod defects - Drawing defects
Rolled-in scale - 1.4003 steel - Cold drawing defects
Rolled-in scale - 1.7707 steel - Cold drawing defects
Rolling fin - 1.2381 steel - Cold drawing defects
Rolling fin - 1.6582 steel - Cold drawing defects
Roughness - Wire rod defects - Drawing defects
Rust scars - 1.7077 steel - Cold drawing defects
Rust scars and corrosion - 1.4301 steel - Cold drawing defects
Scab on the surface - 1.7034 steel - Cold drawing defects
Scab out of foreign material - 1.4305 steel - Cold drawing defects
Scabs on the surface - 1.4305 steel - Cold drawing defects
Scabs on the surface - 1.4305 steel - Cold drawing defects
Scale - Wire rod defects - Drawing defects
Scale pits with grain boundary oxidation - 1.4303 steel - Cold drawing defects
Scale pits with grain boundary oxidation - 1.4303 steel - Cold drawing defects
Scale scars through too long annealing time - 1.4305 steel - Cold drawing defects
Scratch after grinding - 1.4104 steel - Cold drawing defects
Scratches - Wire rod defects - Drawing defects
Segregate-free, martensite-free 4615 modified that extruded wthout failures - Drawing defects
Segregation - Drawing defects
Sharpened slag line - 1.8519 steel - Cold drawing defects
Shear cracks at a pressed part - 1.5513 steel - Cold drawing defects
Shell - Wire rod defects - Drawing defects
Shells - Drawing defects
Shrink hole - 1.4301 steel - Cold drawing defects
Shrink hole with scale - 1.2343 steel - Cold drawing defects
Slag under the surface - 1.4105 steel - Cold drawing defects
Slag under the surface - 1.7707 steel - Cold drawing defects
Slags and titanium carbides - 1.4872 steel - Cold drawing defects
Slivers and cracks - Drawing defects
Solid abrasive was pressed into the surface - 1.4301 steel - Cold drawing defects
Strecher-strains in cold formed carbon steel sheet range component - Drawing defects
Stress corrosion cracking at a screw - 1.4404 steel - Cold drawing defects
Stress crack - 1.8519 steel - Cold drawing defects
Stress crack after the roll cooling - 1.2550 steel - Cold drawing defects
Stress crack after the rolling - 1.2357 steel - Cold drawing defects
Stress crack at a helical spring - 1.8159 steel - Cold drawing defects
Stress crack at the wire - 1.7707 steel - Cold drawing defects
Stress crack in a nitrided component - 1.8507 steel - Cold drawing defects
Stress crack on the rod wire - 1.8523 steel - Cold drawing defects
Strip with porosity - 1.2201 steel - Cold drawing defects
Strong corrosion at chain links - 1.4571 steel - Cold drawing defects
Strong grain boundary oxidation - 1.2201 steel - Cold drawing defects
Strong pickling attack - 1.4105 steel - Cold drawing defects
Strong pickling attack with grain boundary attack - 1.4567 steel - Cold drawing defects
Strong slag line - 1.3520 steel - Cold drawing defects
Strong slag line - 1.4718 steel - Cold drawing defects
Surface bursts at a tensile test - 1.7131 steel - Cold drawing defects
Surface cracks at the drawing - 1.4301 steel - Cold drawing defects
Surface decarburisation - Wire rod defects - Drawing defects
Surface defects in a strip after hot rolling - Drawing defects
Surface near slag - 1.4301 steel - Cold drawing defects
Torn at the drawing - 1.4305 steel - Cold drawing defects
Torn wire at the drawing - 1.7176 steel - Cold drawing defects