Sacrificial protection
Reduction of corrosion of a metal in an electrolyte by galvanically coupling it to a more anodic metal; a form of cathodic protection.

Salt fog test
An accelerated corrosion test in which specimens are exposed to a fine mist of a solution usually containing sodium chloride, but sometimes modified with other chemicals.

Salt spray test
See salt fog test.

Saturated calomel electrode
A reference electrode composed of mercury, mercurous chloride (calomel), and a saturated aqueous chloride solution.

Scaling
(1) The formation at high temperatures of thick corrosion product layers on a metal surface. (2) The deposition of water-insoluble constituents on a metal surface.

Season cracking
An obsolete historical term usually applied to stress-corrosion crackling of brass.

Selective leaching
Corrosion in which one element is preferentially removed from an alloy, leaving a residue (often porous) of the elements that are more resistant to the particular environment. Also called dealloying or parting. See also decarburization, decobbaltification, denickelification, dezincification, and graphitic corrosion.

Sensitizing heat treatment
A heat treatment, whether accidental, intentional, or incidental (as during welding), that causes precipitation of constituents at grain boundaries, often causing the alloy to become susceptible to intergranular corrosion or intergranular stress-corrosion cracking. See also sensitization.

Sensitization
In austenitic stainless steels the precipitation of chromium carbides, usually at grain boundaries, on exposure to temperatures of about 550 to 850 ºC (about 1000 to 1550 ºF), leaving the grain boundaries depleted of chromium and therefore susceptible to preferential attack by a corroding (oxidizing) medium.

Shear
That type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact.

Shear strength
The stress required to produce fracture in the plane of cross section, the conditions of loading being such that the directions of force and of resistance are parallel and opposite although their paths are offset a specified minimum amount. The maximum load divided by the original cross-sectional area of a section separated by shear.

Sigma phase
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section.

Sigma-phase embrittlement
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 560 and 980 ºC ( 1050 and 1800 ºF). Sigma-phase embrittlement results in severe loss in toughness and ductility, and can make the embrittled material susceptible to intergranular corrosion. See also sensitization.

Slip
Plastic deformation by the irreversible shear displacement (translation) of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide.

Slow strain rate technique
An experimental technique for evaluating susceptibility to stress-corrosion cracking. It involves pulling the specimen to failure in uniaxial tension at a controlled slow strain rate while the specimen is in the test environment and examining the specimen for evidence of stress-corrosion cracking.

Slushing compound
An obsolete term describing oil or grease coatings used to provide temporary protection against atmospheric corrosion.

Smelt
Molten slag; in the pulp and paper industry, the cooking chemicals tapped from the recovery boiler as molten material and dissolved in the smelt tank as green liquor.

S-N diagram
A plot showing the relationship of stress, S, and the number of cycles, N, before fracture in fatigue testing.

Soft water
Water that is free of magnesium or calcium salts.

Solder embrittlement
Reduction in mechanical properties of a metal as a result of local penetration of solder along grain boundaries.

Solid-metal embrittlement
The occurrence of embrittlement in a material below the melting point of the embrittling species. See also liquid-metal embrittlement.

Solid solution
A single, solid, homogeneous crystalline phase containing two or more chemical species.

Solute
The component of either a liquid or solid solution that is present to a lesser or minor extent: the component that is dissolved in thesolution.

Solution
In chemistry,a homogeneous dispersion of two or more kinds of molecular or ionic species. Solution may be composed of any combination of liquids, solids, or gases, but they always consist of a single phase.

Solution heat treatment
Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution.

Solution potential
Electrode potential where half-cell reaction involves only the metal electrode and its ion.

Solvent
The component of either a liquid or solid solution that is present to a greater or major extent; the component that dissolves the solute.

Sour gas
A gaseous environment containing hydrogen sulfide and carbon dioxide in hydrocarbon reservoirs. Prolonged exposure to sour gas can lead to hydrogen damage, sulfide-stress cracking, and/or stress-corrosion cracking in ferrous alloys.

Sour water
Waste waters containing fetid materials, usually sulfur compounds.

Space Outgassing
Release of contained gas in the vaccum of outer space. eg. rapid destructive expansion of plastics and similar materials.

Space Pitting
Pitting resulting from ablation, outgassing or meteor contact.

Spalling
The spontaneous chipping, fragmentation, or separation of a surtace or surface coating.

Spheroidite
An aggregate of iron or alloy carbides of essentially spherical shape dispersed throughout a matrix of ferrite.

Sputtering
A coating process whereby thermally emitted electrons collide with inert gas atoms, which accelerate toward and impact a negatively charged electrode that is a target of the coating material. The impacting ions dislodge atoms of the target material, which are in turn projected to and deposited on the substrate to form the coating.

Stabilizing treatment
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating, temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 ºC (1600 to 1650 ºF) to precipitate all carbon, as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature.

Standard electrode potential
The reversible potential for an electrode process when all products and reactions are at unit activity on a scale in which the potential for the standard hydrogen half-cell is zero.

Strain
The unit of change in the size or shape of a body due to force. Also known as nominal strain.

Strain-age embrittlement
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200 ºC (400 ºF), but requiring a few hours to a year at room temperature.

Strain aging
Aging induced by cold working.

Strain hardening
An increase in hardness and strength caused by plastic deformation at temperatures below the recrystallization range.

Strain rate
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time.

Stray current
Current flowing through paths other than the intended circuit.

Stray-current corrosion
Corrosion resulting from direct current flow through paths other than the intended circuit. For example, by an extraneous current in the earth.

Stress
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression) or shear. See also residual stress.

Stress concentration factor (K
t
)
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also called theoretical stress concentration factor.

Stress-corrosion cracking (SCC)
A cracking process that requires the simultaneous action of a corrodent and sustained tensile stress. This excludes corrosion-reduced sections that fail by fast fracture. It also excludes intercrystalline or transcrystalline corrosion, which can disintegrate an alloy without applied or residual stress. Stress-corrosion cracking may occur in combination with hydrogen embrittlement.

Stress-intensity factor
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing, a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. Various subscripts are used to denote different loading conditions or fracture toughnesses:
KcPlane-stress fracture toughness. The value of stress intensity at which crack propagation becomes rapid in sections thinner than those in which plane-strain conditions prevail.


KIStress-intensity factor for a loading condition that displaced the crack faces in a direction normal to the crack plane (also known as the opening mode of deformation).


KIc. Plane-strain fracture toughness. The minimum value of Kc for any given material and condition, which is attained when rapid crack propagation in the opening mode is governed by plane-strain conditions.


KIdDynamic fracture toughness. The fracture toughness determined under dynamic loading conditions; it is used as an approximation of KIc for very tough materials.
KISCC.

Threshold stress-intensity factor for stress-corrosion cracking. The critical plane-strain stress intensity at the onset of stress-corrosion cracking under specified conditions.
KQ.

Provisional value for plane-strain fracture toughness.
Kth. Threshold stress intensity for stress-corrosion cracking. The critical stress intensity at the onset of stress-corrosion cracking under specified conditions.
DK. The range of the stress-intensity factor during a fatigue cycle.

Stress-intensity factor range,
D
K.

In fatigue, the variation in the stress-intensity factor in cycle, that is, Kmax-Kmin.

Stress raisers
Changes in contour or discontinuities in structure that cause local increases in stress.

Stress ratio,
A
or
R

The algebraic ratio of two specified stress values in a stress cycle. Two commonly used stress ratios are: (1) the ratio of the alternating stress amplitude to the mean stress. A = Sa/Sm and (2) the ratio of the minimum stress to the maximum stress. R =Smin/Smax.

Stress-relief cracking
Also called postweld heat treatment cracking, stress-relief cracking occurs when susceptible alloys are suhjected to thermal stress relief after welding to reduce residual stresses and improve toughness. Stress-relief cracking occurs only in metals that can precipitation-harden during such elevated-temperature exposure; it usually occurs at stress raisers, is intergranular in nature, and is generally observed in the coarse-grained region of the weld heat-affectted zone. See also cold cracking, hot cracking, and lamellar tearing.

Stress relieving
Heat treatment carried out in steel to reduce internal stresses.

Striation
A fatigue fracture feature, often observed in electron micrographs, that indicates the position of the crack front after each succeeding cycle of stress. The distance between striations indicates the advance of the crack front across that crystal during one stress cycle, and a line normal to the striation indicates the direction of local crack propagation. See also beach marks.

Subsurface corrosion
Formation of isolated particles of corrosion products beneath a metal surface. This results from the prcferential reactions of certain alloy constituents to inward diffusion of oxygen, nitrogen, or sulfur.

Sulfidation
The reaction of a metal or alloy with a sulfur-containing species to produce a sulfur compound that forms on or beneath the surface on the metal or alloy.

Sulfide stress cracking
Brittle failure by cracking under the combined action of tensile stress and corrosion in the presence of water and hydrogen sulfide. See also environmental cracking.

Surfactant
A surface-active agent; usually an organic compound whose moleculei contain a hydrophilic group at one end and a lipophilic group at the other.